Preparation and Property of Self⁃Crosslinkable Water⁃Based Polyacrylic Dispersion
Li Lan, Cui Xi, Yu Qihong, Bian Jianghai, Wang Yang, Shi Dongjian, Zhang Hongji, Dong Weifu
Abstract485)   HTML    PDF (2023KB)(282)      
By using methyl methacrylate (MMA) as the harder monomer, butyl acrylate (BA) as the softer monomer, acrylic acid (AA) as the functional monomer, acetoacetoxyethyl methacrylate (AAEM) as the crosslinking monomer, tert⁃butyl peroxybenzoate as the initiator, propylene glycol butyl ether as the solvent for prepared self⁃crosslinking acrylate emulsion by free radical solution polymerization and phase inversion, and the emulsion could be self⁃crosslinked after baking at high temperature without additional crosslinking agent. This article mainly studied the influence of acrylic acid, acetoacetoxyethyl methacrylate and curing time on the performance of the polyacrylic resin dispersion and the film property. The results show that the optimized formula is as follows: The dosage of AA and AAEM are 3.5% and 5.0% of the total monomer mass, respectively, and the baking time is 1.0 h at a curing temperature of 180 ℃. FT⁃IR and GPC analysis showed that AAEM was successfully attached to the molecular chain of acrylic resin; SEM and particle size analyzer analysis showed that the TG of the film is latex particles were spherical and uniformly distributed; DSC analysis showed that after the synthesized resin dispersion is significantly increased after the synthesized resin dispersion is baked at high temperature for a period of time.
2021, 41 (1): 1-7. DOI: 10.3969/j.issn.1672-6952.2021.01.001
Research on the Quality Evaluation of Revenue Information Based on Entropy Weight⁃TOPSIS:Taking Company X as an Example
Cui Xiaoling, Hu Qiaqia, Zhang Qiwang
Abstract225)   HTML    PDF (738KB)(105)      
Taking X company as the research object, this paper constructed the evaluation index system of revenue information quality which was more fitted with the actual situation of X company. It evaluated the revenue information quality of X company from 2014 to 2017 by using entropy weight⁃TOPSIS method. It proved that the evaluation results accorded with the actual operation of X company, which provided development direction for the company's value promotion and sustainable development. Taking 2017 as an example, this paper made a comprehensive evaluation of the industry revenue quality, which provided a method reference for the comprehensive evaluation of enterprise income quality.
2020, 40 (5): 86-91. DOI: 10.3969/j.issn.1672-6952.2020.05.015
Pilot-Scale Integrative Membrane Bioreactor System for Municipal Wastewater Treatment
CHEN Jing-run, LIU Zhi-hong, CUI Xiu-xia, ZHANG Hong-lin, LIU Dan
Abstract400)      PDF (1518KB)(279)      
A 110 days'experiment was carried out to study a pilot-scale integrative A/O(anaerobic/ aerobic) MBR treating domestic wastewater from an university. Influent wastewater was stopped from day 51 to day 56 and the activated sludge was feeded by faecula and urea, and inlet was restarted on day 57. Chemical Oxygen Demand(COD),Biochemical Oxygen Demand(BOD5),Ammonia Nitrogen(NH+4N) and Total Phosphorus (TP) concentration was investigated in different part of the system. The average removal efficiency of COD,BOD5, ρ(NH+4-N),TP was 95.10%,90.96%,93.02% and 93.37%, respectively, mainly digested in anoxic tank. MLSS and SV in the aeroic tank increased gradually and stayed steadily on 8 600 mg/L and 85%, respectively. SVI was lower than 112.1 mg/L during the whole experiment. The value of MLVSS/MLSS, which reflects the sludge activity, descended slightly in 110 days'study, especially on the anaphase. The results shows a promising future for the application of this system for municipal wastewater reclamation.
2009, 29 (1): 8-10.